HX380LAD+Z is a high-strength steel grade with exceptional mechanical and chemical properties, making it a desirable material for engineering applications. The mechanical composition of HX380LAD+Z steel grade typically includes a high tensile strength, yield strength, and elongation, which all contribute to its excellent performance in structural and mechanical engineering. Specifically, HX380LAD+Z steel grade has a […]

Mechanical composition: – Yield strength: 380 MPa – Tensile strength: 450-530 MPa – Elongation: 23% – Hardness: HRB 70-90 Chemical composition: – Carbon (C): 0.08% – Manganese (Mn): 1.8% – Phosphorus (P): 0.08% – Sulfur (S): 0.015% – Silicon (Si): 0.15% – Aluminum (Al): 2% (min) – Zinc (Zn): 60-200 g/m^2 The HX380LAD+Z steel grade […]

The strong and durable HX380LAD+Z steel grade is commonly used in automotive applications due to its high strength and excellent formability. The mechanical composition of this steel grade includes a minimum yield strength of 380 MPa and a minimum tensile strength of 450-560 MPa. It also has good elongation properties, typically around 21-24%. The chemical […]