Архиви на ознаки: HC340LA steel grade

HC340LA is a high-strength, low-alloy steel grade that is designed to meet the demands of modern engineering and design. It offers excellent formability and weldability, making it suitable for a wide range of applications in the automotive, construction, and manufacturing industries. Mechanical Composition: – Tensile strength: 410-510 MPa – Yield strength: 340-420 MPa – Elongation: […]

Innovative Techniques for Forming and Welding HC340LA Steel Grade Mechanical Composition: – Tensile Strength: 410-510 MPa – Yield Strength: 290-360 MPa – Elongation: 23-28% – Hardness: 140-190 HB Chemical Composition: – Carbon (C): 0.12% max – Manganese (Mn): 1.00% max – Phosphorus (P): 0.035% max – Sulfur (S): 0.025% max – Silicon (Si): 0.50% max […]

Chemical Composition: – Carbon (C): ≤0.15% – Manganese (Mn): 1.20-1.50% – Phosphorus (P): ≤0.025% – Sulfur (S): ≤0.015% – Silicon (Si): 0.50-0.80% – Aluminum (Al): ≥0.015% Mechanical Properties: – Tensile Strength: 410-510 MPa – Yield Strength: ≥340 MPa – Elongation: ≥23% – Hardness: ≤170 HB HC340LA is a high-strength, low-alloy steel with good formability and […]

HC340LA is a high-strength steel grade that is well-suited for use in high-stress applications. It offers good formability and weldability, making it a versatile choice for a variety of industrial applications. Mechanical Composition: – Tensile Strength: 410-510 MPa – Yield Strength: 290-360 MPa – Elongation: 23-27% Chemical Composition: – Carbon (C): 0.15% max – Manganese […]

Environmental Benefits: 1. Reduced carbon footprint: HC340LA steel grade has a high strength-to-weight ratio, which means less steel is needed to achieve the same structural integrity. This results in lower transportation emissions and reduced overall carbon footprint. 2. Increased recyclability: HC340LA steel grade is highly recyclable, meaning that it can be reused in future construction […]

HC340LA is a high-strength low-alloy (HSLA) steel that is revolutionizing the metalworking industry due to its exceptional mechanical and chemical properties. This steel grade offers improved formability, weldability, and high strength, making it highly desirable for a wide range of applications. Mechanical Composition: – Tensile strength: 410-510 MPa – Yield strength: 340 MPa – Elongation: […]

The mechanical composition of HC340LA steel grade typically includes a yield strength of 340 MPa, a tensile strength of 410-510 MPa, and an elongation of 20-23%. This indicates that the material is relatively strong and ductile, making it suitable for various construction and fabrication applications. The chemical composition of HC340LA steel grade typically includes elements […]

HC340LA is a high-strength, low-alloy steel grade with excellent formability and weldability. It is commonly used in automotive components, construction materials, and other structural applications where strength and durability are essential. The mechanical composition of HC340LA steel typically includes a minimum yield strength of 340 MPa and ultimate tensile strength of 420-510 MPa. Its elongation […]

HC340LA steel grade is a high-strength low-alloy (HSLA) steel that is widely used in automotive manufacturing due to its superior mechanical and chemical properties. Mechanical Composition: – High tensile strength: HC340LA steel has a minimum yield strength of 340 MPa, which makes it suitable for automotive components that require high strength and rigidity. – Superior […]

Physical Properties: – Density: 7.85 g/cm3 – Melting point: 1420-1460°C – Thermal conductivity: 43 W/mK – Electrical conductivity: 52.5 x 106 S/m Mechanical Properties: – Tensile strength: 410-510 MPa – Yield strength: ≥ 340 MPa – Elongation: ≥ 23% – Hardness: ≤ 170 HB Chemical Composition: – Carbon (C): ≤ 0.1% – Manganese (Mn): 1.00-1.50% […]