Mechanical composition: – Yield strength: 220 MPa – Tensile strength: 270-360 MPa – Elongation: 34-38% – Nodal steel number: 1.0923 Chemical composition: – Carbon (C): 0.08% – Manganese (Mn): 1.40% – Phosphorus (P): 0.080% – Sulfur (S): 0.015% – Silicon (Si): 0.080% – Aluminum (Al): 0.015% – Zinc (Z): 0.20% Innovative uses in construction and […]
Category Archives: Galvanized steel
The Superior Properties of HX220YD+Z Steel for Automotive Applications Mechanical Composition: – Tensile Strength: 300-400 MPa – Yield Strength: 220 MPa – Elongation: 20-25% – Hardness: 60-70 HRB Chemical Composition: – Carbon: 0.08% – Manganese: 1.5% – Phosphorus: 0.08% – Sulfur: 0.03% – Silicon: 0.15% – Aluminum: 0.015% – Zinc: 30 g/m2 (coating weight) These […]
HX220YD+Z is a high-strength steel grade with excellent formability and durability, commonly used in automotive and construction industries. This steel grade is known for its outstanding mechanical properties and chemical composition, making it ideal for various applications. Mechanical Composition: – Tensile Strength: 220-280 MPa – Yield Strength: 220 MPa – Elongation: 34% – Hardness: HRB […]
Mechanical Composition: – Tensile strength: 780-950 MPa – Yield strength: 720-810 MPa – Elongation: 10-15% – Hardness: 250-350 HV Chemical Composition: – Carbon (C): 0.15% max – Manganese (Mn): 2.0% max – Phosphorus (P): 0.025% max – Sulfur (S): 0.010% max – Silicon (Si): 0.5% max – Aluminum (Al): 0.015% max – Chromium (Cr): 1.0% […]
– Introduction to DP (Dual-Phase) steel grades – Chemical composition of HCT780X(DP800) steel grade – Mechanical properties of HCT780X(DP800) steel grade – Microstructure and phase distribution of HCT780X(DP800) steel grade – Performance and applications of HCT780X(DP800) steel grade – Conclusion and future prospects
HCT780X(DP800) is a dual phase steel grade with a high strength and good formability, making it suitable for a variety of manufacturing applications. The mechanical composition of HCT780X(DP800) steel grade typically includes a tensile strength of 780-950 MPa and a yield strength of 700-800 MPa. This high strength allows for the use of thinner and […]
The HCT780X(DP800) steel grade is a high-strength, dual-phase steel specifically designed for use in vehicle safety applications. It offers a combination of high strength and good formability, making it an ideal choice for applications where both crashworthiness and lightweight design are important. Mechanical Composition: – Tensile Strength: 780-950 MPa – Yield Strength: 690-830 MPa – […]
Mechanical Composition: – Yield strength: 780 MPa – Tensile strength: 900-1050 MPa – Total elongation: 10-15% – Minimum bending radius: 0.5t (t= material thickness) Chemical Composition (approximate values): – Carbon (C): 0.2% – Manganese (Mn): 2.5% – Silicon (Si): 0.6% – Phosphorus (P): 0.08% – Sulfur (S): 0.015% – Aluminum (Al): 0.2% – Titanium (Ti): […]
The HCT780X(DP800) steel grade is a dual-phase high-strength steel that exhibits exceptional mechanical properties, making it suitable for use in advanced engineering applications. The mechanical composition of HCT780X(DP800) steel grade includes a tensile strength of at least 780 MPa and a minimum yield strength of 800 MPa. This high strength is achieved through a unique […]
The Rise of HCT780X(DP800) Steel Grade: A Game-Changer in the Automotive Industry Mechanical Composition: – Tensile strength: 780-950 MPa – Yield strength: 600-690 MPa – Elongation: 14-17% – Hardness: 190-220 HB Chemical Composition: – Carbon: 0.13-0.20% – Manganese: 2.50-3.00% – Phosphorus: ≤ 0.080% – Sulfur: ≤ 0.015% – Silicon: 0.15-0.60% – Chromium: ≤ 0.40% – […]