Aŭtoraj Arkivoj: protokol

Mechanical composition: – Yield strength: 380 MPa – Tensile strength: 450-530 MPa – Elongation: 23% – Hardness: HRB 70-90 Chemical composition: – Carbon (C): 0.08% – Manganese (Mn): 1.8% – Phosphorus (P): 0.08% – Sulfur (S): 0.015% – Silicon (Si): 0.15% – Aluminum (Al): 2% (min) – Zinc (Zn): 60-200 g/m^2 The HX380LAD+Z steel grade […]

The strong and durable HX380LAD+Z steel grade is commonly used in automotive applications due to its high strength and excellent formability. The mechanical composition of this steel grade includes a minimum yield strength of 380 MPa and a minimum tensile strength of 450-560 MPa. It also has good elongation properties, typically around 21-24%. The chemical […]

HX340LAD+Z steel grade is a high-strength, low-alloy steel that is specifically designed for use in construction projects where efficiency and cost-effectiveness are essential. This steel grade offers a variety of mechanical and chemical properties that make it an ideal choice for construction applications. Mechanical Composition: – Yield strength: 340 MPa – Tensile strength: 420-510 MPa […]

Mechanical Composition: – Yield Strength: 340 MPa – Tensile Strength: 420-510 MPa – Elongation: 23% – Minimum bending radius: 0.2t Chemical Composition: – Carbon (C): 0.08% – Manganese (Mn): 1.50% – Phosphorus (P): 0.010% – Sulfur (S): 0.015% – Silicon (Si): 0.15% – Aluminum (Al): 1.00% – Zinc (Zn): 3.00% The HX340LAD+Z steel grade offers […]

Mechanical Composition of HX340LAD+Z Steel Grade: – Tensile Strength: 340-420 MPa – Yield Strength: 270-340 MPa – Elongation: 27%-32% – Hardness: 140-190 HB Chemical Composition of HX340LAD+Z Steel Grade: – Carbon (C): 0.15% max – Manganese (Mn): 1.00% max – Phosphorus (P): 0.025% max – Sulfur (S): 0.015% max – Silicon (Si): 0.50% max – […]

Innovative Applications of HX340LAD+Z Steel Grade in Architecture and Design Mechanical Composition: – Tensile strength: 340-420 MPa – Yield strength: 340 MPa – Elongation: 24% – Hardness: HRB 65-85 – Bending radius: 0t-1t Chemical Composition: – Carbon (C): 0.12% – Manganese (Mn): 1.50% – Phosphorus (P): 0.025% – Sulfur (S): 0.015% – Silicon (Si): 0.50% […]

The mechanical composition of HX340LAD+Z steel grade includes a yield strength of 340 MPa, a tensile strength of 410-510 MPa, and an elongation of 23-27%. This indicates the steel’s ability to withstand significant loads and deformations before reaching its breaking point. The chemical composition of HX340LAD+Z steel grade typically includes elements such as carbon, manganese, […]

Mechanical Composition of HX340LAD+Z Steel Grade: – Tensile Strength: 340-420 MPa – Yield Strength: 270-350 MPa – Elongation: 27-35% – Hardness: HRB 60-85 – Impact Strength: >200 J Chemical Composition of HX340LAD+Z Steel Grade: – Carbon (C): 0.11% – Manganese (Mn): 1.00% – Phosphorus (P): 0.045% – Sulfur (S): 0.045% – Silicon (Si): 0.50% – […]

HX340LAD+Z steel grade is the ultimate choice for structural engineering due to its excellent mechanical and chemical composition. Mechanically, HX340LAD+Z steel grade offers high strength, good formability, and excellent weldability, making it ideal for structural applications where strength and flexibility are crucial. Its mechanical composition includes a minimum yield strength of 340 MPa, a minimum […]

Specification: HX340LAD+Z is a high-strength low-alloy steel grade with superior formability and weldability, making it a sustainable solution for industrial manufacturing. This steel grade meets the requirements of EN 10346:2015 and is specifically designed for cold forming operations. Mechanical Composition: – Yield strength: 340-420 MPa – Tensile strength: 420-510 MPa – Elongation: 23-32% – R-value: […]